119
Table A 4: Figure 4.25 High speed tensile impact resistance standard deviation data, polymer matrix CMR 648.
Sample ID Standard deviation of the impact resistance (KJ/ m2) Wood content and size Wt % ratio PPgMA/ EvOH content
6/0 5/1 3/3 1/5 0/6
30 % 180 um 0.05 0.05 0.05 0.08 0.04
10 % 180 um 0.06 0.10 0.17 0.11 0.10
30 % Less 180 um 0.08 0.05 0.06 0.04 0.05
10 % Less 180 um 0.10 0.15 0.09 0.05 0.03
Table A 5: Figure 4.26 Tensile strength, max stress standard deviation data, polymer matrix CMR 648.
Sample ID Standard deviation of the max stress (MPa) Wood content and
size
Wt % ratio PPgMA/ EvOH content
6/0 5/1 3/3 1/5 0/6
30 % 180 um 0.88 0.85 0.92 0.43 0.51
10 % 180 um 1.17 0.56 0.33 1.23 0.37
30 % Less 180 um 4.12 0.69 0.98 0.68 0.90
10 % Less 180 um 0.53 1.24 0.84 0.31 0.37
Table A 6: Figure 4.27 Tensile strength, max % strain standard deviation data, polymer matrix CMR 648.
Sample ID Standard deviation of the max % strain Wood content and
size
Wt % ratio PPgMA/ EvOH content
6/0 5/1 3/3 1/5 0/6
30 % 180 um 0.19 0.56 1.28 0.51 0.71
10 % 180 um 0.49 1.22 1.38 1.43 1.53
30 % Less 180 um 1.50 0.44 0.47 0.25 0.19
10 % Less 180 um 1.55 1.02 1.07 0.59 1.71